In Accordance With: NB/T47018-2011 GB/T5293-1999 F5AZ-H08A F5A2H08MnA
AWS-A5.17 F7AZ-EL12 F7A2-EM12K
Welding flux is needed while submerged arc wire welding.
There are SJ101, SJ301 and SJ501 in our warehouse.
Description:
Agglomerated flux SJ501 is a kind of acid aluminum-titanium type sintered flux, the basicity index is
about 0.8. It is shaped as black, round grains and its grain size is 2.0-0.28mm (10-60Mesh). It can be
used with either AC or DC. The welding wire is connected to the positive electrode when used with DC. It
has stable combustion, good slag detachability and good appearance of weld. It has a thick skin to a
small quality of rust and high temperature oxidation film on account of strong the capability of resist pore.
As a peculiar production technique is adopted, the flux possesses better moisture resistance and
good strength of grains, which may satisfy the requirements for regular transportation, storage and
recycling use in welding. The flux has less specific gravity when it is bulk packed. And it is consumed
less during the welding.
Usage:
1. for low carbon, low alloy and pipeline steel.
2. for thick wall structures of different high-tensile steels.
Cautions:
1.The oil contamination, moisture, iron rust and other foreign substances must be removed from the
welding joint.
2. It is better to weld under direct current.
3. Welding flux must be baked under 300-350°C for more than 2 hours before usage.
Chemical Compositions:
Al2O3+MnO |
CaO+MgO |
SiO2+TiO2 |
CaF2 |
S |
P |
25~30 |
25~30 |
15~20 |
15~20 |
≤0.03 |
≤0.03 |
Notes for welding:
1. Redry the flux for 2 hours at 300-350º C prior to be used.
2. Some rust, oil, moisture and other impurities must be cleared away from the area to be welded.
Application:
With suitable welding wires(H08MnA. H08MnMoA. H10Mn2), it can welding common structural steel, boiler
steel, pipeline steel, etc. The flux can be used for multiple fast welding, and can be suitable for single-
sided welding, especially suitable for pressure vessel, such as oil and gas pipes, tanks and cylinders of
automatic submerged arc welding.
(Mechanical Performance of the Deposited Metal):
Wires |
Standard Models |
бs(Mpa) |
бb(Mpa) |
δ5 |
Akv(J) |
HO8A |
F4A2-HO8A |
≥330 |
≥420 |
≥22% |
≥27 |
HO8MnA |
F5A2-HO8MnA |
≥400 |
≥500 |
≥22% |
≥27 |
Fit |
GB/T5293-1999 |
F4A2-H08A |
F5A2-H08MnA |
Equivalent to |
AWS-A5·17 |
F6A2-EL12 |
F7A3-EM12 |
Mechanical Property:(according to GB5293-1999 F4A1-H08A)
Test Item |
Tensile Strength (MPa) |
Yield Strength (MPa) |
Elongation (%) |
Impact Absorption Rate (J) |
-40οC |
Guaranteed Value |
410~550 |
≥330 |
≥22.0 |
≥27 |
Our Service:
1. Samples: Samples are available for you. We will send you samples as your requirements.
2. If you have any questions, we can explain to you immediately.
3. We promise we will supply our best quality with factory price.
4. We promise the goods can be delivered on time and will not bring any trouble to you.
5. When you use our products, we can guide you how to use them.
6. We will try our best to service you well as your requirements.
How to contact us?
Mr. Jacky-MIGHTY QINGDAO METAL MATERIALS CO., LTD.
Tel: +86-0532-66010291
Mobile: +86-15764260250
Add: Room705, Building A, Heda Office Building, NO. 175, Tailiu Road, Shibei Strict, Qingdao, China